Fullerene derivatives and their metal complexes

ABSTRACT

A fullerene derivative, with a solubility in n-hexane of not lower that 0.1 mg/ml at 25° C., includes a fullerene skeleton and three or more organic groups attached to the fullerene skeleton, where each of the organic groups is represented by the general formula (III): 
 
CH 2 —X (R 2 )(R 3 )(R 4 )  (III) 
 
where X represents an element belonging to the group 14 in the periodic table; and R 2 , R 3  and R 4  may be the same or different and each represents a hydrogen atom, hydrocarbon group, alkoxy group or amino group.

FIELD OF THE INVENTION

The present invention relates to a fullerene derivative having an extremely high solubility in an organic solvent and a metal complex comprising a molecule and/or anion of fullerene derivative as a ligand.

BACKGROUND OF THE INVENTION

Since a method for the synthesis of a large amount of C₆₀ was established in 1990, extensive studies have been made of fullerene. As a result, numerous fullerene derivatives have been synthesized and their various functions have been made obvious. With this technical progress, the development of various uses of electronic conductor, semiconductor, bioactive material, etc. comprising fullerene derivatives has been under way (for general remarks, see “Gendai Kagaku (Modern Chemistry)”, April 1992, page 12, and June 2000, page 46, Chem. Rev., 1998, 98, 2527, etc.).

The inventors have synthesized various fullerene compounds comprising ten organic groups connected to the fullerene skeleton (hereinafter occasionally referred to as “derivative bearing 10 attached organic groups” or “10-fold adduct”) and various fullerene compounds comprising five organic groups connected to the fullerene skeleton (hereinafter occasionally referred to as “derivative bearing 5 attached organic groups” or “5-fold adduct”) and reported them (see Japanese Patent Laid-Open No. 1998-167994, Japanese Patent Laid-Open No. 1999-255509, Japanese Patent Laid-Open No. 2002-241323, J. Am. Chem. Soc. 1996, 118, 12850, Org. Lett. 2000, 2, 1919, Chem. Lett. 2000, 1098). The inventors have also synthesized fullerene compounds comprising three organic groups connected to the fullerene skeleton (hereinafter occasionally referred to as “derivative bearing 3 attached organic groups” or “3-fold adduct”) and reported these compounds, including their metal complexes, separately of the aforementioned fullerene compounds (see Japanese Patent Laid-Open No. 1999-255508, J. Am. Chem. Soc. 1998, 120, 8285, Org. Lett. 2000, 2, 1919.).

In order to apply fullerene derivatives to various purposes, it is extremely useful to render them soluble in an organic solvent. It is thought that a fullerene derivative having a high solubility in an organic solvent, if obtained, can be applied to uses requiring dissolution in an organic solvent such as intermediate which is subjected to further transformation to synthesize other derivatives, electronic industrial material and ligand of metal complex, making it possible to drastically expand the application of fullerene derivatives.

However, all various known fullerene derivatives, including those disclosed in the above cited references, have an extremely low solubility in an ordinary organic solvent having a relatively small polarity. It is thus disadvantageous in that the solvent applicable when these fullerene derivatives are applied to the aforementioned various purposes is restricted, making the application of these fullerene derivatives extremely difficult or substantially impossible. Under these circumstances, a fullerene derivative having a high solubility in an organic solvent has been desired.

SUMMARY OF THE INVENTION

The invention has been worked out in the light of the aforementioned problems. An aim of the invention is to provide a fullerene derivative having a high solubility in an ordinary organic solvent and a metal complex comprising as a ligand, a molecule and/or anion of such a fullerene derivative.

The inventors made extensive studies of fullerene derivatives having an improved solubility in an organic solvent to solve the aforementioned problems. As a result, it was found that a fullerene derivative having a specific organic group exhibits an extremely high solubility in an organic solvent. The invention has thus been worked out.

In other words, the essence of the invention lies in a fullerene derivative having a solubility in n-hexane of not lower than 0.1 mg/ml at 25° C. and a metal complex comprising a molecule and/or anion of fullerene derivative as a ligand and having a solubility in n-hexane of not lower than 0.1 mg/ml at 25° C.

DETAILED DESCRIPTION OF THE INVENTION

The invention will be further described hereinafter.

The fullerene derivative of the invention is a compound which is derived from fullerene and has an extremely high solubility in an organic solvent.

The term “fullerene” as used herein is meant to indicate a carbon cluster comprising carbon atoms in a spherical or Rugby ball configuration. Specific examples of fullerene include C₆₀ (so-called Buckministerfullerene), C₇₀, C₇₆, C₇₈, C₈₂, C84, C₉₀, C₉₄, C₉₆ and higher carbon clusters. The fullerene which is the skeleton of the fullerene derivative of the invention is not specifically limited. From the standpoint of availability of reactive starting materials to be used for production, C₆₀ or C₇₀ is desirable. The method for the production of fullerene is not specifically limited. Fullerenes produced by any known methods can be used as starting materials of fullerene derivatives. The fullerene of the invention may be a purified single compound or a mixture of two or more fullerenes.

The term “organic solvent” as used herein is meant to indicate a solvent which belongs to the group of organic compounds and is generally used for the dissolution of organic materials. Specific examples of the organic solvent include hydrocarbons such as pentanes, hexanes, heptanes, benzene, toluene and xylenes, esters such as methyl acetate, ethyl acetate, methyl propionate and ethyl propionate, ethers such as diethyl ether, dibutyl ether and tetrahydrofuran, halohydrocarbons such as dichloromethane, chloroform, dichloroethanes, chlorobenzene and dichlorobenzenes, alcohols such as methanol, ethanol and butanols, amides and ureas such as N,N-dimethylformamide, N,N,N′,N′-tetramethylurea and γ-butyrolactam, and mixed solvents of two or more thereof.

The fullerene derivative of the invention has a high solubility in all or some of the aforementioned organic solvents. In order to secure the specific objectivity, the solubility in n-hexane as one of organic solvents at 25° C. is employed as a parameter showing solubility in organic solvent that defines the fullerene derivative of the invention.

The solubility in n-hexane at 25° C. is determined as follows. In some detail, a predetermined amount of n-hexane is added to a fullerene derivative. The mixture is then stirred at 25° C. for 1 hour. The resulting slurry is then subjected to centrifugal separation. The solution is then decanted. The solvent is then distilled off the resulting supernatant liquid. The resulting precipitate is dried in vacuo, and then measured for weight. Thus, the solubility in n-hexane at 25° C. is calculated.

The fullerene derivative of the invention is characterized in that it normally has a solubility in n-hexane of not lower than 0.1 mg/ml, preferably not lower than 1 mg/ml, more preferably not lower than 10 mg/ml, particularly not lower than 50 mg/ml at 25° C. as determined according to the aforementioned method.

The fullerene derivative of the invention is not limited in its structure so far as it has a solubility falling within the above defined range. A specific preferred example of the fullerene derivative is a fullerene derivative comprising one organic group or a plurality of organic groups added to the fullerene skeleton (hereinafter occasionally referred to as “adduct”, “added derivative” or hereinafter occasionally referred to as “3-fold adduct”, “5-fold adduct” or “10-fold adduct” depending upon the number of organic groups added to the fullerene skeleton (prefix number represents the number of organic groups added)). The term “organic group” as used herein is a general term for groups containing carbon. The term “addition” as used herein is meant to indicate the addition of groups to the bond in the fullerene skeleton resulting in the formation of a bond.

The aforementioned fullerene derivative comprising one organic group or a plurality of organic groups added to the fullerene skeleton will be further described hereinafter.

The kind of the organic groups to be added to the fullerene skeleton (hereinafter occasionally referred to as “attached organic group”) is not specifically limited, but various organic groups may be used. In practice, however, organic groups having a structure mainly composed of a hydrocarbon some of the carbon atoms of which are optionally replaced by elements other than carbon belonging to the group 14 in the periodic table (18-group long form of the periodic table), particularly silicon, are used. The number of elements including carbon belonging to the group 14 is preferably large. In some detail, it is preferred that four or more elements be present per attached organic group. In particular, the sum of the number of carbon and silicon atoms is preferably from 4 to 20, more preferably from 5 to 18. The attached organic group may contain hetero-substituents such as halogen group, alkoxy group and amino group.

Attached organic groups mainly composed of aliphatic hydrocarbon structure tend to exhibit a higher solubility in an organic solvent than attached organic groups mainly composed of aromatic hydrocarbon structure even if the added number of attached organic groups are the same. Another tendency is that the more branches the attached organic group has, the higher is the solubility of the adduct in an organic solvent.

The attached organic group in the fullerene derivative of the invention is preferably an organic group which is connected to the fullerene skeleton via methylene group, i.e., organic group having the following structure: —CH₂—R₁  (I) wherein R₁ represents a hydrogen atom or organic group.

The reason why the structure represented by the general formula (I) is desirable is uncertain. However, the reason is presumably because the methylene group present in the bond to the fullerene skeleton allows free rotation of R₁, thereby preventing the fullerene derivative molecules from approaching each other in the organic solvent and hence from undergoing molecular interaction.

In particular, R₁ in the general formula (I) preferably has a structure represented by the following general formula (II). In other words, typical attached organic group in the fullerene derivative has following formula (III): X(R₂)(R₃)(R₄)  (II) —CH₂—X(R₂)(R₃)(R₄)  (III) wherein X represents an element belonging to the group 14 in the periodic table. Specific examples of this element include C, Si, Ge, Sn, and Pb. Preferred among these elements are C and Si, particularly Si. R₂, R₃ and R₄ each independently represents a hydrogen atom, hydrocarbon group, alkoxy group or amino group. Preferably, all of R₂, R₃ and R₄ are elements other than hydrogen atom, i.e., hydrocarbon group, alkoxy group or amino group. R₂, R₃ and R₄ may be the same or different.

The reason why the structure represented by the general formula (II) is desirable is uncertain. The reason is presumably because R₂, R₃ and R₄ occupy a relatively large space, thereby preventing the fullerene derivative molecules from approaching each other in the organic solvent and hence from undergoing molecular interaction.

Specific examples of the attached organic group in the fullerene derivative of the invention include n-pentyl group, isopentyl group, neopentyl group, 3-phenylpropyl group, 2,2-diethylpropyl group, (trimethylsilyl)methyl group, (phenyldimethylsilyl)methyl group, and (triethylsilyl)methyl group. Preferred among these attached organic groups are neopentyl group, (trimethylsilyl)methyl group, and (triethylsilyl)methyl group because they satisfy the general formula (I) and can be easily incorporated in the fullerene skeleton at a step during the synthesis of fullerene derivative. Particularly preferred among these attached organic groups are (trimethylsilyl)methyl group, and (triethylsilyl)methyl group because they also satisfy the general formula (II) or (III).

The number of these attached organic groups to be added to the fullerene skeleton is not specifically limited but may be arbitrarily selected from the group consisting of 1 or more. It is preferred that the number of attached organic groups to be added to the fullerene skeleton be greater because the fullerene which is a skeleton can be easily rendered soluble in an organic solvent. In some detail, the number of attached organic groups to be added to the fullerene skeleton is preferably 3 or more. In particular, as described later, the number of attached organic groups to be added to the fullerene skeleton is preferably 3, 5 or 10 because derivative bearing 3 attached organic groups, derivative bearing 5 attached organic groups and derivative bearing 10 attached organic groups can be selectively synthesized by properly selecting the method for addition reaction. When the number of attached organic groups to be added to the fullerene skeleton is plural, these attached organic groups may be the same or different.

The fullerene derivative of the invention can be produced by any of various methods depending on its structure. For example, a fullerene derivative comprising one or a plurality of organic groups added to the fullerene skeleton (derivative bearing attached organic groups) can be produced by introducing organic groups into fullerene skeleton by various known methods.

The introduction of attached organic groups into fullerene can be effected by nucleophilic addition by way of example. In some detail, addition reaction may be effected in the presence of a Grignard reagent, an organolithium reagent or an organocopper reagent prepared from such a reagent and a copper compound at one step or multiple steps. The structure of Grignard reagent, organic lithium reagent and organocopper reagent are not specifically limited. In other words, a Grignard reagent or an organic lithium reagent having an organic group to be incorporated may be used to effect direct addition reaction. Alternatively, in the case where such a Grignard reagent or an organic lithium reagent can be difficultly synthesized or is unstable, a group which can be easily incorporated may be incorporated in the fullerene skeleton which is then subjected to conversion reaction so that the substituent is converted to the desired organic group. In the case where the organic group to be incorporated in the presence of such a reagent has a structure satisfying the general formula (I) or (II), it is more desirable that none of R₂, R₃ and R₄ be a hydrogen atom.

Numerous combinations of relative positions at which the organic groups are added to the fullerene skeleton are possible. The addition pattern is not specifically limited. However, it is known that as 3-fold adduct, 5-fold adduct and 10-fold adduct there can be selectively synthesized adducts having structures represented by the following general formulae (IV), (V) and (VI), respectively. Therefore, from the standpoint of ease of synthesis, adducts having these structures are preferably produced.

wherein R₅ to R₇ may be the same or different and each independently represents an organic group.

wherein R₈ to R₁₂ may be the same or different and each independently represents an organic group.

wherein R₁₃ to R₂₂ may be the same or different and each independently represents an organic group.

In the case where addition reaction is effected in the presence of an organic copper reagent as shown by the following general formula (VII), the resulting primary product is presumably the corresponding organic copper compound. The fullerene derivative of the invention is isolated in the form of protonated compound normally by reacting this primary product with a protonic compound such as H₂O.

(The general formula (VII) is illustrated with reference to the synthesis of 5-fold adduct of fullerene by way of example, but the invention is not limited to 5-fold adduct. Further, the general formula (VII) is illustrated with all of the attached organic groups added to the fullerene skeleton represented by R. The plurality of R's may be hereinafter the same or different unless otherwise specified.)

This protonated compound is a preferred embodiment of the fullerene derivative of the invention. The protonated compound which has once been isolated is then reacted with alkyllithium, etc. so that it is easily deprotonated to lithiated compound as represented by the following general formula (VIII). By adding an electrophilic reagent to this lithiated compound, it can be converted to another preferred form of fullerene derivative. For example, the lithiated compound can be alkylated with an alkylation reagent, etc. to an alkylated compound. These products obtained by electrophilic reaction, too, are other preferred embodiments of the fullerene derivative of the invention.

wherein E⁺ represents a reagent having electrophilic reactivity.

The fullerene derivative of the invention exhibits as an extremely a high solubility in an organic solvent as not lower than 0.1 mg/ml in n-hexane at 25° C. Therefore, when dissolved in an organic solvent, the fullerene derivative of the invention can be substantially handled in the same manner as for ordinary organic compounds. Further, the fullerene derivative of the invention can be used for purposes requiring dissolution in an organic solvent such as intermediate which is subjected to further transformation to synthesize other derivatives, electronic industrial material and ligand of metal complex and thus is extremely useful. Accordingly, the fullerene derivative of the invention can be expected to be widely applied to arts which have heretofore difficultly allowed the utilization of fullerene derivatives.

The metal complex comprising a molecule and/or anion of fullerene derivative as a ligand will be further described hereinafter. This metal complex has a molecule and/or anion of fullerene derivative as a ligand and exhibits a high solubility in an organic solvent. As a parameter of the solubility of the metal complex in an organic solvent, the solubility of the metal complex in n-hexane at 25° C. is defined to secure a specific objectivity as mentioned above. In some detail, the metal complex of the invention normally exhibits a solubility in n-hexane of not lower than 0.1 mg/ml, preferably not lower than 1 mg/ml at room temperature (typically 25° C.).

The metal complex of the invention is not limited in its structure and complex form so far as it exhibits a high solubility in an organic solvent as mentioned above. The metal complex of the invention preferably has a molecule and/or anion of the fullerene derivative of the invention as detailed above as a ligand. In particular, compounds comprising the aforementioned 3-fold adduct, 5-fold adduct or 10-fold adduct of fullerene having the following structure with cyclopentadienyl anion position are desirable from the standpoint of ease of synthesis.

-   -   wherein MXn represents a metal fragment in which M represents a         metal atom selected from the group consisting of alkali metal,         alkaline earth metal, transition metal, Sn and Tl, X represents         a ligand such as molecule or ion attached to the metal atom M,         and n represents a number of not smaller than 0.

Specific examples of M include Li, Na, K, Ba, Sn, Sc, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Zr, Ru, Rh, Pd, Ag, Cd, Hf, Ta, W, Re, Pt, Au, Hg, Tl, and Sm. Preferred among these metal atoms are Li, K, Ba, Ti, Fe, Cu, Zr, Ru, Rh, Pd, and Hf.

Specific examples of X include neutral ligands including ethers such as THF (tetrahydrofuran) and dimethoxyethane, phosphines such as trimethylphosphine and triphenylphosphine, nitriles such as acetonitrile, CO and olefins such as ethylene and cyclooctadiene, halogen atoms such as Cl and Br, alkoxy groups such as hydride, methoxy, ethoxy and butoxy, amide groups such as dimethylamide and diethylamide, alkyl groups such as methyl, ethyl and butyl, phenyl group, substituted phenyl groups, and sulfonate groups such as tosylate.

The proper ligand X and the number n of the ligands X are determined by the properties and valency of the metal atom M. The plurality of X's, if any, may be the same or different.

The metal complex of the invention can be produced by various methods depending on the structure thereof. In some detail, a proper metal precursor can be acted on the lithiated compound of fullerene derivative represented by the general formula (VIII) as shown by the general formula (X) to synthesize a metal complex of the invention having a corresponding fullerene derivative as a ligand. The aforementioned lithiated compound itself, too, is an embodiment of the metal complex of the invention.

The metal complex of the invention has a molecule and/or anion of fullerene derivative as a ligand and thus is provided with inherent properties of fullerene derivative. The metal complex of the invention also exhibits as extremely a high solubility in an organic solvent as not lower than 0.1 mg/ml in n-hexane at 25° C. and thus can be used for various purposes requiring dissolution in an organic solvent and is extremely useful. Accordingly, the metal complex of the invention can be expected to be widely applied to arts which have heretofore difficultly allowed the utilization of fullerene derivatives.

The invention will be further described in the following examples, but the invention is not limited thereto so far as it does not depart from the scope thereof.

EXAMPLE 1

Synthesis of C₆₀[CH₂Si(CH₃)₃]₅H

As shown in Scheme 1, in an atmosphere of nitrogen, 100 mg of C₆₀ was dissolved in 15 ml of o-dichlorobenzene. The solution was then reacted with a copper reagent prepared from 16 equivalents of a trimethylsilylmethyl magnesium chloride Grignard reagent (CH₃)₃SiCH₂MgCl in diethylether (concentration: about 1.0 M) and 18 equivalents of a copper (I) bromide-dimethyl sulfide complex CuBr.S(CH₃)₂ at 0° C. After 1 hour, to the reaction solution was added 0.1 ml of a saturated aqueous ammonium chloride solution to quench the reaction. After the termination of the reaction, the reaction solution was concentrated to about 15 ml. The reaction solution was diluted with 50 ml of toluene, and then passed through a silica gel plug with toluene as an eluent to remove magnesium salts and other by-products. The solvent was then distilled off until about 2 ml of the solvent was left. To the reaction solution was then added 200 ml of methanol to cause reprecipitation. As a result, a 5-fold trimethylsilylmethyl adduct (C₆₀[CH₂Si(CH₃)₃]₅H) having a purity of 97% was obtained (isolated yield: 97%).

wherein Me represents a methyl group (—CH₃).

NMR Data of C₆₀[CH₂Si(CH₃)₃]₅H

¹H-NMR (C₆D₆, 30° C.)

-   -   0.16 (s, 9H, Si(CH₃)₃),     -   0.21 (s, 18H, Si(CH₃)₃),     -   0.23 (s, 18H, Si(CH₃)₃),     -   2.10 (d, ²J_(H—H)=14.8 Hz, 2H, CH₂),     -   2.17 (s, 2H, CH₂),     -   2.18 (s, 2H, CH₂),     -   2.25 (s, 2H, CH₂),     -   2.34 (d, ²J_(H—H)=14.8 Hz, 2H, CH₂),     -   4.70 (s, 1H, H(Cp))

¹³C-NMR (C₆D₆, 30° C.):

-   -   0.57 (Si(CH₃)₃)     -   0.57 (Si(CH₃)₃)     -   0.62 (Si(CH₃)₃)     -   31.55 (CH₂),     -   31.94 (CH₂),     -   38.71 (CH₂),     -   53.38 (CH₃C),     -   53.66 (CH₃C),     -   55.26 (CH₃C),     -   63.63 (HC(Cp)),         143.05, 143.87, 143.90, 144.11, 144.36, 144.65, 145.56, 145.63,         145.87, 146.37, 146.64, 147.23, 147.45, 147.52, 148.09, 148.12,         148.40, 148.59, 148.67, 149.03, 149.11, 149.26, 150.12, 150.88,         154.22, 154.46, 154.69, 157.88

Comparison of compounds which have been already known, i.e., C₆₀(CH₃)₅H and C₆₀(C₆H₅)₅H in signal of proton at cyclopentadiene moiety in CDCl₃ showed the following data:

-   -   C₆₀ (CH₃)₅H, 4.46 ppm     -   C₆₀(CH₂Si(CH₃)₃)₅H, 4.56 ppm     -   C₆₀(C₆H₅)₅H, 5.30 ppm         Properties of C₆₀[CH₂Si(CH₃)₃]₅H

Brown powder. When it stayed solid, it was stable at room temperature in the air.

Solubility of C₆₀[CH₂Si(CH₃)₃]₅H

To 100 mg of C₆₀[CH₂Si(CH₃)₃]₅H was added 0.5 ml of n-hexane. The mixture was then stirred at 25° C. for 1 hour. The slurry was purified, and then subjected to centrifugal separation by a centrifugal separator. The resulting supernatant liquid was withdrawn. The solvent was then distilled off. The residue was then dried in vacuo. The weight of the residue was then measured. The result was 32.5 mg. Accordingly, the solubility of this compound in n-hexane at room temperature (25° C.) can be calculated to be 65 mg/ml.

EXAMPLE 2

Synthesis of C₆₀{CH₂Si(CH₃)₃}₃H

As shown in Scheme 2, in dried air, 0.5 g of C₆₀ was dissolved in 150 ml of o-dichlorobenzene. The solution was then reacted with 8 equivalents of a trimethylsilylmethyl magnesium chloride Grignard reagent (CH₃)₃SiCH₂MgCl in an ether (concentration: about 1.0 M) at room temperature (25° C.). After 2 hours, to the reaction solution was added 0.5 ml of a saturated aqueous ammonium chloride solution to quench excessive Grignard reagent. The solvent was then distilled off under reduced pressure at 70° C. The resulting precipitate was then dissolved in 100 ml of toluene. The reaction solution was then passed through a silica gel plug with toluene as an eluent to remove magnesium salts and other by-products. When toluene was distilled off, a 2-fold trimethylsilylmethyl adduct C₆₀{CH₂Si(CH₃)₃}₂ having a purity of 70% was obtained. The product was then extracted with hot n-hexane. As a result, substantially pure C₆₀{CH₂Si(CH₃)₃}₂ was obtained. The isolated yield was 54%.

In an atmosphere of argon, 170 mg of C₆₀{CH₂Si(CH₃)₃}₂ thus obtained was dissolved in 20 ml of o-dichlorobenzene. The reaction solution was then reacted with 5 equivalents of trimethylsilylmethyl magnesium chloride Grignard reagent ((CH₃)₃SiCH₂MgCl) in an ether (concentration: about 1.0 M) at room temperature (25° C.). After 1 hour, to the reaction solution was added 0.2 ml of a saturated aqueous ammonium chloride solution to quench the reaction. The solvent was then distilled off under reduced pressure at 70° C. The resulting precipitate was then dissolved in 20 ml of toluene. The reaction solution was then passed through a silica gel plug with toluene as an eluent to remove magnesium salt and other by-products. When toluene was then distilled off, a 3-fold trimethylsilylmethyl adduct C₆₀{CH₂Si(CH₃)₃}₃H having a purity of about 50% was obtained. The 3-fold trimethylsilylmethyl adduct was then subjected to fractionation with HPLC (eluent: toluene/2-propanol=7/3) equipped with a column (BuckyPrep, produced by Nacalai Tesque Co., Ltd.) to obtain pure C₆₀{CH₂Si (CH₃)₃}₃H. The isolated yield of C₆₀{CH₂Si(CH₃)₃}₃H from C₆₀{CH₂Si(CH₃)₃}₂ was 37%. The total yield of C₆₀{CH₂Si(CH₃)₃}₃H from C₆₀ was 20%.

wherein Me represents a methyl group (—CH₃).

NMR data of C₆₀{CH₂Si(CH₃)₃}₃H

¹H-NMR (CDCl₃, 30° C.):

-   -   0.07 (s, 9H, Si(CH₃)₃),     -   0.21 (s, 18H, Si(CH₃)₃),     -   2.06 (d, ²J_(H—H)=14.4 Hz, 1H, CH₂),     -   2.24 (d, ²J_(H—H)=14.4 Hz, 1H, CH₂),     -   2.29 (d, ²J_(H—H)=14.4 Hz, 1H, CH₂),     -   2.29 (d, ²J_(H—H)=14.4 Hz, 1H, CH₂),     -   2.38 (d, J_(H—H)=14.4 Hz, 1H, CH₂),     -   2.40 (d, J_(H—H)=14.4 Hz, 1H, CH₂),     -   5.30 (s, 1H, H(Cp))

¹³C-NMR (C₆D₆, 30° C.):

-   -   0.25 (q, ¹J_(C—H)=129 Hz, Si(CH₃)₃),     -   0.30 (q, ¹J_(C—H)=129 HZ, Si(CH₃)₃),     -   0.50 (q, ¹J_(C—H)=129 Hz, Si(CH₃)₃),     -   31.21 (t, ¹J_(C—H)=132 Hz, CH₂),     -   32.59 (t, ¹J_(C—H)=132 Hz, CH₂),     -   38.08 (t, ¹J_(C—H)=132 Hz, CH₂)     -   52.92 (s, CCH₂),     -   54.97 (s, CCH₂),     -   56.85 (s, CCH₂),     -   61.98 (d, ¹J_(C—H)=136 Hz, HC(Ind)),     -   133.88-162.98         Properties of C₆₀{CH₂Si(CH₃)₃}₃H

Brown powder. When it stayed solid, it was stable at room temperature in the air.

Solubility of C₆₀{CH₂Si(CH₃)₃}₃H

The solubility of C₆₀{CH₂Si(CH₃)₃}₃H in n-hexane at room temperature (25° C.) was measured under the same conditions as in Example 1. The result was 11 mg/ml.

EXAMPLE 3

Synthesis of Rh[C₆₀{CH₂Si(CH₃)₃}₃](1,5-cyclooctadiene)

8.0 mg (0.0081 mmol) of the 3-fold adduct (C₆₀{CH₂Si(CH₃)₃}₃H) of Example 2 was dissolved in 5.0 ml of THF. To the solution was then added a THF solution of 1.2 equivalents of potassium t-butoxide at room temperature. When the reaction mixture was stirred for 10 minutes, a green solution of C₆₀{CH₂Si(CH₃)₃}₃K was produced. To the solution was then added 1.0 equivalent (4.0 mg or 0.0081 mmol) of {Rh(1,5-cyclooctadiene)Cl}₂ at room temperature. The reaction mixture was then stirred for 10 minutes. The solvent was then distilled off. The precipitate was then extracted with toluene to obtain a metal complex. Toluene was then distilled off. The resulting solid was then washed with n-hexane to obtain pure Rh[C₆₀{CH₂Si(CH₃)₃}₃](1,5-cyclooctadiene). The isolated yield of Rh[C₆₀{CH₂Si (CH₃)₃}₃](1,5-cyclooctadiene) from {C₆₀[CH₂Si(CH₃)₃}₃H was 91%.

NMR data of Rh[C₆₀{CH₂Si(CH₃)₃}₃](1,5-cyclooctadiene)

¹H-NMR (CDCl₃, 30° C.):

-   -   0.08 (s, 9H, Si(CH₃)₃),     -   0.11 (s, 18H, Si(CH₃)₃),     -   1.77 (d, ²J_(H—H)=14 Hz, 2H, CH₂),     -   2.04 (d, ²J_(H—H)=14 Hz, 2H, CH₂),     -   2.43 (br s, 8H, cod),     -   2.44 (d, ²J_(H—H)=14 Hz, 2H, CH₂),     -   4.19 (br s, 2H, cod),     -   5.62 (br s, 2H, cod)         Other Data of Rh[C₆₀{CH₂Si(CH₃)₃}₃](1,5-cyclooctadiene)     -   APCl-Mass (+) m/z=1194 (M⁺)     -   UV-vis: λmax=705 nm         Solubility of Rh[C₆₀{CH₂Si(CH₃)₃}₃](1,5-cyclooctadiene)

The solubility of Rh[C₆₀{CH₂Si(CH₃)₃}₃](1,5-cyclooctadiene) in n-hexane at room temperature (25° C.) was measured under the same conditions as in Example 1. The result was 5.0 mg/ml.

COMPARATIVE EXAMPLE 1

The solubility of C₆₀ produced by Aldrich Co., Ltd. was measured under the same conditions as in Example 1. The result was less than 0.001 mg/ml. Thus, this product was little dissolved in n-hexane.

COMPARATIVE EXAMPLE 2

(C₆H₅)₅C₆₀H was synthesized according to the method described in Example 1 of Japanese Patent Laid-Open No. 1998-167994. The solubility of (C₆H₅)₅C₆₀H thus obtained was measured under the same conditions as in Example 1 of the invention. The result was less than 0.001 mg/ml. Thus, this product was little dissolved in n-hexane.

COMPARATIVE EXAMPLE 3

(CH₃)₅C₆₀H was synthesized according to the method described in Example 1 of Japanese Patent Laid-Open No. 1999-255509. The solubility of (CH₃)₅C₆₀H thus obtained was measured under the same conditions as in Example 1 of the invention. The result was less than 0.001 mg/ml. Thus, this product was little dissolved in n-hexane.

REFERENCE EXAMPLE 1

The solubility of C₆₀[CH₂Si(CH₃)₃]₂ (known in J. Org. Chem. 1994, 59, 1246), which is an intermediate product of Example 2, was measured under the same conditions as in Example 1. The result was about 0.05 mg/ml. The solubility of this intermediate product measured at 50° C. under the same conditions as in Example 1 was about 0.2 mg/ml. Thus, as described in Example 2, this fullerene derivative can be withdrawn by extraction with hot n-hexane.

The fullerene derivative of the invention exhibits as an extremely a high solubility in an organic solvent as not lower than 0.1 mg/ml in n-hexane at 25° C. Therefore, the fullerene derivative of the invention can be used for purposes requiring dissolution in an organic solvent such as intermediate which is subjected to further transformation to synthesize other derivatives, electronic industrial material and ligand of metal complex and thus is extremely useful.

The metal complex of the invention has a molecule and/or anion of fullerene derivative as a ligand and exhibits as extremely a high solubility in an organic solvent as not lower than 0.1 mg/ml in n-hexane at 25° C. Therefore, as a metal complex having functions characteristic to fullerene derivative, the metal complex of the invention can be used for various purposes requiring dissolution in an organic solvent such as catalyst and electronic industrial material and is extremely useful.

While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.

This application is based on Japanese patent application No. 2002-016144 filed on Jan. 24, 2002, the entire contents thereof being hereby incorporated by reference. 

1-11. (canceled)
 12. A The metal complex according to claim 16 wherein the metal complex has a solubility in n-hexane of not lower than 0.1 mg/ml at 25° C.
 13. The metal complex according to claim 12, wherein the solubility is not lower than 1 mg/ml.
 14. The metal complex according to claim 12, wherein the fullerene skeleton is C₆₀.
 15. (canceled)
 16. A metal complex comprising at least one ligand selected from the group consisting of a molecule of a fullerene derivative, and an anion of the fullerene derivative, said wherein the fullerene derivative comprises a fullerene skeleton and three or more organic groups attached to the fullerene skeleton, wherein each of the organic groups is represented by the general formula (III): —CH₂—X(R₂)(R₃)(R₄)  (III) where X represents an atom belonging to the group 14 in the periodic table; and R₂, R₃ and R₄ may be the same or different and each represents a hydrogen atom, hydrocarbon group, alkoxy group or amino group. 